Oil Sintered Bronze Bushing

Powder metallurgy (PM) is a forming and fabrication technique consisting of three major processing stages.
First, the primary material is physically powdered, divided into many small individual particles.
Next, the powder is injected into a mold or passed through a die to produce a weakly cohesive structure (via cold welding) very near the dimensions of the object ultimately to be manufactured.
Pressures of 10-50 tons per square inch are commonly used. Also,to attain the same compression ratio across more complex pieces, it is often necessary to use lower punches as well as an upper punch.
Finally, the end part is formed by applying pressure,high temperature,long setting times (during which self-welding occurs), or any combination thereof.

►Bronze Material
 

Basic Materials	Chemical Composition (%)	Other Materials
SAE841 ASTM B438-70 GR1 Type DIN30910 PART3 SINT A50 Mil-B-5687C Type… Comp	Cu: 87.5~90.5, Fe: 1.0max, Sn:9.5~10.5, P:1.75, Particles:0.5	MPIF: CT- 1000 - K19 / ASTM: B 438 - 83a MPIF: CT - 1000 - K26 / ASTM: B 438 - 83a / DIN: SINT - A50 MPIF: CT - 1000 - K37 / ASTM: B 438 - 83a / DIN: SINT - B50 MPIF: CT - 1001 - K23 / ASTM: B 438 - 83a / DIN: SINT - B51 MPIF: CT - 1001 - K33 / ASTM: B 438 - 83a / DIN: SINT - C51 MPIF: CTG - 1004 - K10 MPIF: CTG - 1004 - K15

►Contact information

Hunan Jintai Hardware And Machinery Co.,Ltd
Rm.426, Hunan International Commerce Centre,Jintai Square,410001 Changsha,Hunan,P.R.China
Contact: Ms. Susan Shi

Mob(whatsapp): 0086 13517489983

Email: susan@slide-bearing.com